Scotch-Weld

TM

Epoxy Adhesives

DP125 Translucent and Gray

Product Description

3M™ Scotch-Weld™ Epoxy Adhesive DP125 Translucent is a faster curing version

of the 3M™ Scotch-Weld™ Epoxy Adhesive 2216 Translucent B/A. The worklife

and cure time has been reduced from hours and days for the Scotch-Weld epoxy

adhesive 2216 Translucent B/A to minutes and hours. Final shear and peel strengths

remain similar or even slightly improved compared to the Scotch-Weld epoxy

adhesive 2216 Translucent.

Scotch-Weld epoxy adhesive DP125 Gray is a filled, pigmented version of the

Scotch-Weld epoxy adhesive DP125 Translucent and has similar performance and

flexibility properties.

Available in bulk containers as 3M™ Scotch-Weld™ Epoxy Adhesive 125 B/A

Translucent and 125 B/A Gray.

Features

• 25 minute worklife

• High peel and shear strength

• Flexible

• Controlled flow (gray)

• Translucent or Gray

• 1:1 mix ratio

Typical Uncured

Properties

Note: The following technical information and data should be considered representative

or typical only and should not be used for specification purposes.

3M™ Scotch-

Weld™ Epoxy

Adhesive DP125

Translucent

3M™ Scotch-

Weld™ Epoxy

Adhesive

DP125 Gray

Base Resins

Epoxy/Amine

Epoxy/Amine

@ 80°F

Accelerator (A)

2,000-8,000 cps

22,000-33,000 cps

35,000-75,000 cps

45,000-65,000 cps

Net Weight

Base (B)

(Lbs./gal.)

Accelerator (A)

9.3-9.7

8.4-8.6

10.3-10.7

8.5-8.9

Color

Base (B)

Accelerator (A)

Clear

Amber

Gray

Amber

Mix Ratio (B:A)

By Volume

By Weight

1:1

1.10:1

1:1

1.2:1

2 gram

@ 73°F

20 gram

25 min.

18 min.

25 min.

15 min.

Footnotes: Viscosity determined using 3M test method C-1d. Procedure involves Brookfield RVF, #7 spindle, 20 rpm and

80°F. Measurement taken after 1 minute.

1. Worklife determined using 3M test method C-3180. Procedure involves periodically measuring a 2 gram mixed mass for self

leveling and wetting properties. This time will also approximate the usable worklife in an

3M™ EPX Applicator mixing nozzle.

Technical Data

March 2019