Low Odor Acrylic Adhesives

DP810 • DP810 Black • DP810NS

- 4 -

Test Methods and

Footnotes

1) Viscosity obtained by Brookfield, DV-II, #7 Spindle, 20 rpm at 75°F(24°C).

2) Overlap Shear Test Method: overlap shear test for adhesion determined in

accordance to ASTM D1002-72, sample dimensions were 1" x 4" x 1/8", with a

1/2 square inch area of overlap, bonded to themselves unless otherwise noted,

allowed to cure for at least 6 hours at 75°F (24°C) before testing. Data were

collected using a Sintech 5GL Mechanical Tester with a 2000# or 5000# load

cell. Test rate was 0.1"/minute. Strength determined at 75°F (24°C) unless

otherwise noted.

3) Peel tests (ASTM D1876-61T) on FPL etched, 0.032” gauge aluminum, with a

.017" bondline thickness. Jaw separation rate 20"/min. All bonds were allowed to

cure for at least 6 hours at 75°F (24°C) before testing.

4) Environmental tests were conducted by immersing bonded coupons prepared in

accordance to description in footnote 2.