Plastic and Rubber Instant Adhesives

PR40 • PR100 • PR600 • PR1500 • PR Gel

Hot Strength

Percent of Initial Strength

Temp (F)

PR40

PR100

PR600

PR1500

PR Gel

72

100

100

100

100

100

167

81

89

83

76

84

212

80

54

52

64

41

257

53

16

14

15

13

Handling Information

Surface Preparation

For optimum strength structural bonds, paint, oxide films, oils, dust, mold release

agents, and all other surface contaminants must be completely removed. However,

the amount of surface preparation depends on the required bond strength and the

environmental aging resistance desired by the user. Typical quick surface preparation

would include wiping with a clean solvent (such as isopropyl alcohol*), abrading

the surface with a clean fine abrasive, and then wiping again with a clean solvent to

remove loose particles.

Directions for Use

1. Ensure that parts are clean, dry, and free from oil and grease.

2. An instant adhesive activator may be required if there are bonding gaps

or porous substrate surfaces, if substrates are low surface energy plastics

(e.g., polyethylene, polypropylene) or if substrates have acidic surfaces

(e.g., paper, leather).

3. Bond speed is typically very fast so ensure that parts are properly aligned before

dispensing.

4. Product is normally hand applied from the bottle. Apply sparingly to one surface

and press parts firmly together until handling strength is achieved. As a general

rule, as little cyanoacrylate as possible should be used. Over application will

result in slower cure speed and lower bond strength.

Cured Bond Characteristics

1. Full bond strength will typically be achieved within a 24 hour cure time.

2. Low humidity or low temperature conditions will slow down the cure rate.

3. After curing, 3M™ Scotch-Weld™ Plastic and Rubber Instant Adhesive bonds

are suitable for use up to about 180°F (82°C).

4. Cyanoacrylate bond resistance to most oils and solvents is excellent. Long term

humidity, moisture, or water immersion may affect the strength of a cured

cyanoacrylate bond depending on the substrates and the bond gap. Testing is

recommended to evaluate the effect.

*Note: When using solvents, extinguish all ignition sources, including pilot lights,

and follow the manufacturer’s precautions and directions for use.