L826 SERIES

10. RELIABILITY AND TEST CONDITION :

LCR meter.

Irms(A) will cause the coil temperature rise

approximately

T=40°C without core loss

CH16502, Agilent33420A Micro-Ohm Meter.

1. Applied the allowed DC current

Natural

cooling

Natural

cooling

Isat(A) will cause Lo to drop approximately 20% typical

Solder Temperature : 260±5°C

Solder Temperature : 230±5°C

2. Temperature measured by digital surface thermometer

Measure at room temperature after placing for 2 to 3 hrs.

Measure at room temperature after placing for 2 to 3 hrs.

Measure at room temperature after placing for 2 to 3 hrs.

Measure at room temperature after placing for 2 to 3 hrs.

Applied Current : Rated Curent

10±0.5

seconds

60

seconds

4

Room Temperature

1. Appearance : No damage

2. Inductance : Within ±20% of initial value.

No disconnection or short circuit.

Humidity Resistance

Time : 500±12 hours

Humidity : 90% to 95%

Temperature : 40±5°C

Total : 5 cycles

1. Appearance : No damage

2. Inductance : Within ±20% of initial value.

No disconnection or short circuit.

Life Test

Thermal Shock

Low Temperature

High Temperature

Life Test

Reliability Test

Time : 500±12 hours

Temperature (°C)

Step

Room Temperature

3

2

1

+125±3

-55±3

Conditions of 1 cycle.

Time : 500±12 hours

Temperature : -55±5°C

Temperature : 125±5°C

Preheating Dipping

2. Inductance change : Within ±20%

1. Appearance : No significant abnormality

Solder Heat Resistance

Preheating Dipping

260°C

150°C

Flux for lead free : rosin

Dip Time : 10±0.5sec.

60

seconds

4±1

seconds

Solder : Sn99.95-Cu0.05

Preheat : 150°C, 60sec.

150°C

230°C

More than 90% of the terminal electrode

should be covered with solder.

Solderability Test

Mechanical Performance Test

Saturation Current (Isat)

Heat Rated Current (Irms)

DCR

Dip Time : 4±1sec.

Flux for lead free : rosin

Preheat : 150°C, 60sec.

Solder : Sn99.95-Cu0.05

Within 3

Times (min.)

30±3

Within 3

30±3

TEST CONDITION

HP4284A, CH11025, CH3302, CH1320, CH1320S

Refer to standard electrical characteristics list

PERFORMANCE

Electrical Characteristics Test

ITEM

Inductance

HIGH CURRENT MOLDED POWER INDUCTORS