Application Techniques

• To obtain maximum adhesion, the bonding surfaces must be clean and dry. Isopropyl alcohol is recommended as a

cleaning solvent.*

• Bond strength is dependent upon the amount of adhesive-to-surface contact developed. This wetted area can be increased

by applying 3M™ XYZ-Axis Electrically Conductive Tape 9713 firmly with a roller or finger pressure to exclude air

entrapment. Adhesion is optimized when the substrates are flat or conformable substrates. Adhesion increases after

application, up to 24 hours later, due to increased wetting by the tape.

• Electrical performance is dependent upon the nature of the metal and its surface. Most metal surfaces give enhanced

electrical performance with 3M tape 9713 when the surface has been lightly abraded. Scotch-Brite™ pads are

recommended for preparing the metal surface.

• 3M tape 9713 should be applied between 60°F - 100°F (15°C - 38°C). Tape application below 50°F (10°C) is not

recommended because the adhesive will be too firm to wet the substrates, resulting in low adhesion. Warming the

substrates to 100°F (38°C) facilitates adhesion. Once properly applied, low temperature holding power is generally

satisfactory.

• 3M tape 9713 can be removed by separating the parts using torque for rigid parts or peel for flexible ones. Remove the

adhesive by pulling off as much as possible by hand. Residual adhesive may be removed by rubbing with your finger or

by application of 3M™ Packaging Tape over the residual adhesive followed by removal of the packaging tape. The

surfaces should be cleaned again before applying a new piece of 3M tape 9713. The force required to separate the parts

and/or remove the adhesive can be reduced by softening the adhesive by heating to 158°F -212°F (70°C - 100°C) or using

solvents such as acetone.*

*Note: Carefully read and follow the manufacturer’s precautions and directions for use when handling cleaning solvents.

General Information

3M™ XYZ-Axis Electrically Conductive Tape 9713 provides good adhesion to metal surfaces and provides low electrical

resistance that is stable over time. The pressure sensitive nature and fiber reinforcement of 3M tape 9713 makes this product

convenient to use and 3M tape 9713 also has very good handling properties. 3M tape 9713 also has good liner release.